What is PEEK GLD140 FG natural?
PEEK GLD140 FG natural is a lubricant-modified polyetheretherketone in a food grade compound. An internally embedded solid lubricant significantly reduces the coefficient of friction and wear – for dry-running sliding and guide elements at temperatures up to 250 °C.
Technical data
| Property | Value | Test method |
|---|---|---|
| General Properties | ||
| Density | 1.36 g/cm³ | DIN EN ISO 1183-1 |
| Water absorption | 0.200 % | DIN EN ISO 62 |
| Flammability (Thickness 3 mm / 6 mm) | V0/V0 | UL 94 |
| Mechanical Properties | ||
| Yield stress | 87 MPa | DIN EN ISO 527 |
| Elongation at break | 3 % | DIN EN ISO 527 |
| Tensile modulus of elasticity | 3,700 MPa | DIN EN ISO 527 |
| Notched impact strength | 3.5 kJ/m² | DIN EN ISO 179 |
| Ball indentation hardness | 220 MPa | DIN EN ISO 2039-1 |
| Shore hardness | 86 scale D | DIN EN ISO 868 |
| Thermal Properties | ||
| Melting temperature | 343 °C | ISO 11357-3 |
| Coefficient of linear thermal expansion | 55 ·10⁻⁶/K | DIN 53752 |
| Service temperature, long term | -30 to 250 °C | Average |
| Service temperature, short term (max.) | 310 °C | Average |
| Heat deflection temperature | 150 °C | DIN EN ISO 75, method A, HDT |
PEEK GLD140 FG natural vs. PEEK natural compared directly
| Property | PEEK GLD140 FG natural | PEEK natural |
|---|---|---|
| Density | 1.36 g/cm³ | 1.31 g/cm³ |
| Yield stress | 87 MPa | 110 MPa |
| Elongation at break | 3 % | 20 % |
| Tensile modulus of elasticity | 3,700 MPa | 4000 MPa |
| Shore hardness | 86 scale D | 88 scale D |
| Coefficient of linear thermal expansion | 55 ·10⁻⁶/K | 50 ·10⁻⁶/K |
| Service temperature, long term | -30 to 250 °C | -60 to 250 °C |
| Heat deflection temperature | 150 °C | 152 °C |
PEEK GLD140 FG natural in detail
1What is PEEK GLD140 FG natural?+
PEEK GLD140 FG natural is a lubricant-modified polyetheretherketone in a food grade compound. An internally embedded solid lubricant significantly reduces the coefficient of friction and wear – for dry-running sliding and guide elements at temperatures up to 250 °C. The sliding modification reduces friction and stick-slip effects and considerably improves wear behaviour compared to unfilled PEEK, without compromising resistance to temperature, chemicals and hydrolysis. The modification slightly reduces stiffness, strength and elongation at break compared to standard PEEK; the compound is designed for food contact (see FDA declaration).
2How does Liedtke machine PEEK GLD140 FG natural?+
PEEK GLD140 FG natural can be machined using all conventional cutting methods; because of the high hardness, carbide tools with sharp cutting edges are recommended. Good cooling via chip removal remains important to avoid heat build-up and residual stresses in the part. For tight tolerances and thick-walled parts, we recommend intermediate annealing to relieve machining stresses; thanks to the low moisture absorption, no conditioning is required. For components with food contact, we use food-compatible cooling lubricants and supply with batch traceability on request.
3When should I choose PEEK GLD140 FG natural?+
PEEK GLD140 FG natural is used wherever dry-running sliding elements with food contact are exposed to high temperatures – for example in filling, packaging and baking lines and in mechanical engineering for the food industry:
- Plain bearings, bushings and slide strips
- Guide and format parts in filling and packaging lines
- Wear parts in baking and meat processing lines
4What determines the price of a PEEK GLD140 FG natural part?+
PEEK GLD140 FG natural is calculated individually based on drawing or sample. The part price is determined mainly by the semi-finished form and dimensions, material utilisation and offcuts, machining effort and batch size. We are happy to provide binding prices on request.
5When is PEEK GLD140 FG natural not the right choice?+
The limits of the material are equally important:
- Lower strength and elongation at break than unfilled PEEK
- High material cost compared to engineering plastics
- Not resistant to concentrated sulphuric acid and some halogenated hydrocarbons
6Advantages and disadvantages of PEEK GLD140 FG natural+
An honest assessment:
- Advantage: Internal sliding modification, low coefficient of friction, low wear
- Advantage: Compound designed for food contact
- Advantage: Continuous service up to 250 °C, resistant to steam and cleaning agents
- Advantage: Good dimensional stability, low moisture absorption
- Disadvantage: Lower strength and elongation at break than unfilled PEEK
- Disadvantage: High material cost compared to engineering plastics
- Disadvantage: Not resistant to concentrated sulphuric acid and some halogenated hydrocarbons
Typical properties
- Internal lubricant modification for reduced friction
- Compound suitable for food contact
- Continuous service up to 250 °C
Typical industries
- Food Industry
- Packaging Industry
- Mechanical Engineering
Downloads for PEEK GLD140 FG natural
Related materials
Request a quotation for your PEEK GLD140 FG part
A drawing or a sample is enough. We calculate concretely and advise openly whether PEEK GLD140 FG natural is optimal for your application or an alternative makes more sense.
Send enquiry