What is PA 6 G OL red?
PA 6 G OL red is a cast polyamide 6 special compound, coloured brown-red, with internal oil lubrication. The integrated lubricating oil significantly improves sliding and wear behaviour and prevents stick-slip effects, while maintaining the high toughness of the PA6 G base material.
Technical data
| Property | Value | Test method |
|---|---|---|
| General Properties | ||
| Density | 1.14 g/cm³ | DIN EN ISO 1183-1 |
| Water absorption | 2.00 % | DIN EN ISO 62 |
| Flammability (thickness 3 mm / 6 mm) | HB/HB | UL 94 |
| Mechanical Properties | ||
| Yield stress | 70 MPa | DIN EN ISO 527 |
| Elongation at break | 50 % | DIN EN ISO 527 |
| Tensile modulus | 3,300 MPa | DIN EN ISO 527 |
| Notched impact strength | 4.0 kJ/m² | DIN EN ISO 179 |
| Shore hardness | 82 scale D | DIN EN ISO 868 |
| Thermal Properties | ||
| Melting temperature | 213 °C | ISO 11357-3 |
| Thermal conductivity | 0.25 W/(m·K) | DIN 52612-1 |
| Thermal capacity | 1.70 kJ/(kg·K) | DIN 52612 |
| Coefficient of linear thermal expansion | 80 ·10⁻⁶/K | DIN 53752 |
| Service temperature, long-term | -40 to 110 °C | Average |
| Service temperature, short-term (max.) | 160 °C | Average |
| Heat deflection temperature | 90 °C | DIN EN ISO 75, method A, HDT |
PA 6 G OL red vs. PA 6 G compared directly
| Property | PA 6 G OL red | PA 6 G |
|---|---|---|
| Density | 1.14 g/cm³ | 1.15 g/cm³ |
| Water absorption | 2.00 % | 2.5 % |
| Yield stress | 70 MPa | 75 MPa |
| Elongation at break | 50 % | 45 % |
| Tensile modulus | 3,300 MPa | 3,400 MPa |
| Notched impact strength | 4.0 kJ/m² | 3 kJ/m² |
| Shore hardness | 82 scale D | 83 scale D |
| Melting temperature | 213 °C | 216 °C |
| Coefficient of linear thermal expansion | 80 ·10⁻⁶/K | 80 ·10⁻⁶/K |
| Service temperature, long-term | -40 to 110 °C | -40 to 110 °C |
| Service temperature, short-term (max.) | 160 °C | 170 °C |
| Heat deflection temperature | 90 °C | 95 °C |
PA 6 G OL red in detail
1What is PA 6 G OL red?+
PA 6 G OL red is a cast polyamide 6 special compound, coloured brown-red, with internal oil lubrication. The integrated lubricating oil significantly improves sliding and wear behaviour and prevents stick-slip effects, while maintaining the high toughness of the PA6 G base material. PA 6 G OL red is a cast, semi-crystalline polyamide with an integrated liquid lubricant. The embedded oil provides good sliding properties and reduces friction as well as stick-slip effects, without compromising the basic toughness of the PA6 G base material. Like all polyamides, PA 6 G OL red absorbs moisture from the environment; this makes the material tougher and more impact-resistant, while stiffness and dimensional stability decrease somewhat.
2How does Liedtke machine PA 6 G OL red?+
PA 6 G OL red can be machined like standard PA6 G using all conventional cutting methods; HSS or carbide tools are sufficient. Good cooling via chip removal remains important to avoid softening or smearing of the surface caused by heat build-up. For tight tolerances, we take swelling and shrinkage behaviour into account and condition the semi-finished product where required.
3When should I choose PA 6 G OL red?+
PA 6 G OL red is used wherever good sliding properties and smooth, jerk-free motion without stick-slip effects are needed, for example in mechanical engineering and conveyor technology. The red colouring also makes it easy to visually distinguish from other colour variants.
- Bearing and guide elements
- Components with stick-slip requirements
- Conveyor technology components
4What determines the price of a PA 6 G OL red part?+
PA 6 G OL red is calculated individually based on drawing or sample. The part price is mainly determined by the stock form and dimension, material utilisation (waste), machining effort and batch size. We are happy to quote binding prices on request.
5When is PA 6 G OL red not the right choice?+
Just as important are the limits of the material:
- Moisture absorption of up to 2.0 % in standard atmosphere, causing dimensional and property changes
- Not resistant to strong acids and permanently hot water (hydrolysis)
- Not generally declared for food contact (see FDA declaration)
6Advantages and disadvantages of PA 6 G OL red+
An honest assessment:
- Advantage: Internal oil lubrication for improved sliding and wear behaviour
- Advantage: Good stick-slip properties
- Advantage: High toughness
- Advantage: Good machinability
- Disadvantage: Moisture absorption of up to 2.0 % in standard atmosphere, causing dimensional and property changes
- Disadvantage: Not resistant to strong acids and permanently hot water (hydrolysis)
- Disadvantage: Not generally declared for food contact (see FDA declaration)
Typical properties
- Internal oil lubrication
- Good stick-slip properties
- High toughness
Typical industries
- Mechanical Engineering
- Conveyor Technology
Downloads for PA 6 G OL red
Related materials
Request a quotation for your PA-6-G-OL-red part
A drawing or a sample is enough. We calculate concretely and advise openly whether PA 6 G OL red is optimal for your application or an alternative makes more sense.
Send enquiry